Submonolayer InGaAs/GaAs Quantum Dots Grown by MOCVD

Аннотация

The mode of the growth of InGaAs quantum dots by MOS-hydride epitaxy on GaAs substrates without a deviation and with a deviation of 2° is selected for laser structures emitting at wavelengths above 1.2 μm at room temperature. As a result, a quantum-dot density of 4 × 10¹⁰ cm^–2 is achieved. Stimulated emission is observed in laser structures with seven layers of quantum dots at a wavelength of 1.06 μm at liquid-nitrogen temperature. The threshold power density of optical pumping is about 5 kW/cm².