Conductivity of Ga2O3–GaAs Heterojunctions

Аннотация

The effect of annealing in argon at temperatures of T_an = 700–900°C on the I–V characteristics of metal–Ga₂O₃–GaAs structures is investigated. Samples are prepared by the thermal deposition of Ga₂O₃ powder onto GaAs wafers with a donor concentration of N_d = 2 × 10¹⁶ cm^–3. To measure theI–V characteristics, V/Ni metal electrodes are deposited: the upper electrode (gate) is formed on the Ga₂O₃ film through masks with an area of S_k = 1.04 × 10^–2 cm² and the lower electrode in the form of a continuous metallic film is deposited onto GaAs. After annealing in argon at T_an ≥ 700°C, the Ga₂O₃-n-GaAs structures acquire the properties of isotype n-heterojunctions. It is demonstrated that the conductivity of the structures at positive gate potentials is determined by the thermionic emission from GaAs to Ga₂O₃. Under negative biases, current growth with an increase in the voltage and temperature is caused by field-assisted thermal emission in gallium arsenide. In the range of high electric fields, electron phonon-assisted tunneling through the top of the potential barrier is dominant. High-temperature annealing does not change the electron density in the oxide film, but affects the energy density of surface states at the GaAs–Ga₂O₃ interface.