Piezoresistive and posistor effects in polymer-semiconductor and polymer-ferropiezoceramic composites
- 作者: Mamedov H.1, Parali L.2, Kurbanov M.3, Bayramov A.3, Tatardar F.3, Sabikoglu I.4
-
隶属关系:
- Azerbaijan Technical University
- Department of Electronics and Automation
- Institute of Physics
- Faculty of Arts & Sciences, Departments of Physics
- 期: 卷 50, 编号 5 (2016)
- 页面: 621-626
- 栏目: Amorphous, Vitreous, and Organic Semiconductors
- URL: https://journals.rcsi.science/1063-7826/article/view/197092
- DOI: https://doi.org/10.1134/S1063782616050171
- ID: 197092
如何引用文章
详细
In this study, piezoresistive and posistor effects in polymer-semiconductor and polymer-ferropiezoceramic composites have been investigated. The results show that composites based on crystallizable polymers, such as PVDF, HDPE, and PP dispersed by semiconductors and ferropiezoelectric fillers have piezoresistive and posistor properties, respectively. At low pressure, charge carriers tunneling through the located thin polymer among filler particles into the barrier define the conductivity of the composite. When pressure value is increased from 0 to 1 MPa, the thickness of the interlayer decreases and tunnel conductivity descends exponentially depending on barrier height. The piezoresistor sensitivity of a composite based on PVDF-70 vol % + Si-30 vol % is higher than a composite based on HDPE-70 vol % + Ge-30 vol %. Furthermore, the posistor properties of polymer composites dispersed by ferropiezoceramic are determined as the maximum resistance that varies significantly with temperature. Posistor effect in composites based on polymer + ferropiezoceramic is associated with the height of the barrier layer, which changes according to properties of filler, polymer, and dielectric permittivity of two-phase composites. The highest specific resistance related to HDPE-70 vol % + BaTiO3-30 vol % composite was observed at ~403 K.
作者简介
H. Mamedov
Azerbaijan Technical University
Email: levent.parali@cbu.edu.tr
阿塞拜疆, Baku
L. Parali
Department of Electronics and Automation
编辑信件的主要联系方式.
Email: levent.parali@cbu.edu.tr
土耳其, Turgutlu, Manisa, 45400
M. Kurbanov
Institute of Physics
Email: levent.parali@cbu.edu.tr
阿塞拜疆, Baku
A. Bayramov
Institute of Physics
Email: levent.parali@cbu.edu.tr
阿塞拜疆, Baku
F. Tatardar
Institute of Physics
Email: levent.parali@cbu.edu.tr
阿塞拜疆, Baku
I. Sabikoglu
Faculty of Arts & Sciences, Departments of Physics
Email: levent.parali@cbu.edu.tr
土耳其, Manisa, 45140