Мақаланы E-mail арқылы жіберу Influence of Heat Treatments on the Properties of ZnO Nanorods Prepared by Hydrothermal Synthesis
- Авторлар: Hyunggun Ma 1
-
Мекемелер:
- Department of Electrical and Computer Engineering, Ulsan National Institute of Science and Technology
- Шығарылым: Том 53, № 13 (2019)
- Беттер: 1811-1816
- Бөлім: Fabrication, Treatment, and Testing of Materials and Structures
- URL: https://journals.rcsi.science/1063-7826/article/view/207468
- DOI: https://doi.org/10.1134/S106378261913013X
- ID: 207468
Дәйексөз келтіру
Ашық рұқсат
Рұқсат берілді
Тек жазылушылар үшін
Аннотация
ZnO nanorods were grown on bare or SiO2-coated Si wafers by the hydrothermal method. The ZnO nanorods were annealed at 200, 400, and 600°C, respectively. The structural, optical, and electrical property variation of the ZnO nanorods with the annealing temperature was investigated by X-ray diffraction, field-emission scanning electron microscopy, photoluminescence, and current–voltage measurements. For the ZnO nanorods, compressive strain was detected, which decreased with annealing. Moreover, annealing at 600°C led to nanorod agglomeration. The ZnO nanorods annealed at 400°C exhibited the highest crystallinity.
Негізгі сөздер
Авторлар туралы
Hyunggun Ma
Department of Electrical and Computer Engineering, Ulsan National Institute of Science and Technology
Хат алмасуға жауапты Автор.
Email: hyunggunma@gmail.com
Корей Республикасы, Ulsan, 44919