Structural Transformation of “Silica+Zn” Nanocomposite after Annealing in Oxidizing Atmosphere
- Autores: Komarov F.1, Makhavikou M.1, Vlasukova L.2, Milchanin O.1, Skuratov V.3, Vuuren A.4, Neetling J.4, Parkhomenko I.2, Żuk J.5
-
Afiliações:
- Sevchenko Institute of Applied Physics Problems, Belarusian State University
- Belarusian State University
- Joint Institute for Nuclear Research
- Centre for High Resolution Transmission Electron Microscopy, Nelson Mandela Metropolitan University
- Maria Curie-Skłodowska University
- Edição: Volume 52, Nº 16 (2018)
- Páginas: 2111-2113
- Seção: 26th INTERNATIONAL SYMPOSIUM “NANOSTRUCTURES: PHYSICS AND TECHNOLOGY”. NANOSTRUCTURE TECHNOLOGY
- URL: https://journals.rcsi.science/1063-7826/article/view/205417
- DOI: https://doi.org/10.1134/S1063782618160133
- ID: 205417
Citar
Resumo
It has been found that “hot” high-fluence Zn+ implantation leads to the formation of the extended layer with zinc-based nanoclusters of size up to 10 nm in SiO2 film. The precipitate’s crystalline nature is confirmed by HRTEM studies. Post-implantation annealing at 700°C for 60 min leads to Zn atoms redistribution in implanted region, formation of the larger crystallites (up to 25 nm) and the small Zn nanoparticles surrounded by the oxide shells (core (Zn)/shell(ZnO) structure) as well as the voids formation at the interface “Zn nanocluster/SiO2 matrix”. The number of the core (Zn)/shell (ZnO) structures and the voids increases after annealing at 700°C for 120 min.
Sobre autores
F. Komarov
Sevchenko Institute of Applied Physics Problems, Belarusian State University
Email: m.mohovikov@gmail.com
Belarus, Minsk
M. Makhavikou
Sevchenko Institute of Applied Physics Problems, Belarusian State University
Autor responsável pela correspondência
Email: m.mohovikov@gmail.com
Belarus, Minsk
L. Vlasukova
Belarusian State University
Email: m.mohovikov@gmail.com
Belarus, Minsk
O. Milchanin
Sevchenko Institute of Applied Physics Problems, Belarusian State University
Email: m.mohovikov@gmail.com
Belarus, Minsk
V. Skuratov
Joint Institute for Nuclear Research
Email: m.mohovikov@gmail.com
Rússia, Dubna
A. Vuuren
Centre for High Resolution Transmission Electron Microscopy, Nelson Mandela Metropolitan University
Email: m.mohovikov@gmail.com
República da África do Sul, Port Elizabeth
J. Neetling
Centre for High Resolution Transmission Electron Microscopy, Nelson Mandela Metropolitan University
Email: m.mohovikov@gmail.com
República da África do Sul, Port Elizabeth
I. Parkhomenko
Belarusian State University
Email: m.mohovikov@gmail.com
Belarus, Minsk
J. Żuk
Maria Curie-Skłodowska University
Email: m.mohovikov@gmail.com
Polônia, Lublin