Dynamics of Growth of the Native Oxide of CdxHg1−xTe

Resumo

The growth of the native oxide of the Cd_xHg_1−xTe (MCT) compound is studied by methods of laser and spectral ellipsometry. It is found that a non-absorbing oxide film is formed from the very beginning in the case of MCT oxidation with hydrogen peroxide vapors, whereas oxidation with atmospheric oxygen leads to the formation of absorbing layers on the surface at the first stages of the process. When the oxide film thickness reaches 1–2 nm, the oxidation rate drastically decreases. If MCT samples that were stored for a long time (for years) in air at room temperature are heated at T = 200 °C, the optical thickness of the oxide film decreases.