Wear Resistance of Amorphous-Crystalline Coatings with Lubricants


如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅存取

详细

The results of tests of a Zr–Al–B boundary friction detonation coating in a wide range of changes under friction conditions have been presented. A comparative analysis of the obtained characteristics of friction and wear in order to evaluate the tribotechnical properties of amorphous-crystalline coatings has been carried out. These results have been compared with parallel tests of coatings based on tungsten carbide, samples of hardened steel and bronze, and the bearing of the sliding layer. The formation of solid solutions has been established and the introduction of oxygen in zirconium that corresponds to the formation on the friction surfaces of the secondary structures of the first type, a characteristic feature of which is their surface localization, ultra-dispersed structure, and ability to minimize disruption and shield unacceptable adhesion phenomena. The use of the Auger electron microscope confirmed that oxygen completely replaces the sulfur in the surface structures.

作者简介

V. Babak

Institute of Engineering Thermophysics

编辑信件的主要联系方式.
Email: vdoe@ukr.net
乌克兰, Kyiv, 03057

V. Shchepetov

Institute of Engineering Thermophysics

Email: vdoe@ukr.net
乌克兰, Kyiv, 03057

补充文件

附件文件
动作
1. JATS XML

版权所有 © Allerton Press, Inc., 2018