Abrasive and fretting wear resistance of aluminum alloy specimens manufactured by laser microcladding
- Autores: Tarasova T.V.1, Gvozdeva G.O.1
- 
							Afiliações: 
							- Moscow State Technological University STANKIN
 
- Edição: Volume 38, Nº 3 (2017)
- Páginas: 231-236
- Seção: Article
- URL: https://journals.rcsi.science/1068-3666/article/view/228746
- DOI: https://doi.org/10.3103/S106836661703014X
- ID: 228746
Citar
Resumo
In this article, the results of investigations of abrasive wear resistance and wear under the fretting of the samples obtained by the method of laser microcladding have been presented. The material for sample preparation was powder of Al–Si hypereutectic alloy with the following composition: 70–74 wt % Al and 26–30 wt % Si. The influence of the structure and phase composition of AlSi30 alloy on wear resistance under the conditions of abrasive wear and wear under fretting conditions has been shown.
Palavras-chave
Sobre autores
T. Tarasova
Moscow State Technological University STANKIN
							Autor responsável pela correspondência
							Email: tarasova952@mail.ru
				                					                																			                												                	Rússia, 							Moscow, 127994						
G. Gvozdeva
Moscow State Technological University STANKIN
														Email: tarasova952@mail.ru
				                					                																			                												                	Rússia, 							Moscow, 127994						
Arquivos suplementares
 
				
			 
						 
						 
						 
						 
					 
				 
  
  
  
  
  Enviar artigo por via de e-mail
			Enviar artigo por via de e-mail  Acesso aberto
		                                Acesso aberto Acesso está concedido
						Acesso está concedido Somente assinantes
		                                		                                        Somente assinantes
		                                					