Enviar artigo por via de e-mail The effect of carbamide on the composition of gas phase formed upon thermal destruction of graphite nitrate
- Autores: Ivanov A.1, Filimonov S.1, Shornikova O.1, Malakho A.2
-
Afiliações:
- Department of Chemistry, M. V. Lomonosov Moscow State University
- Institute of New Carbon Materials and Technologies
- Edição: Volume 65, Nº 1 (2016)
- Páginas: 282-286
- Seção: Brief Communications
- URL: https://journals.rcsi.science/1066-5285/article/view/237063
- DOI: https://doi.org/10.1007/s11172-016-1298-y
- ID: 237063
Citar
Acesso aberto
Acesso está concedido
Somente assinantes
Resumo
The composition of gas evolved upon thermal decomposition of individual and carbamidemodified graphite nitrates was determined. The addition of carbamide was shown to result in the 2—4-fold decrease in the content of nitrogen oxides and the 2—5-fold increase in the content of carbon monoxide. The content of nitrogen oxides in the gas phase decreased when the HNO3 : (NH2)2CO molar ratio was equal to 1 : (0.4—1). Combination of carbamide addition with catalytic afterburning provides the 5-fold decrease in the gas-phase amount of nitrogen oxides at the minimum CO content.
Palavras-chave
Sobre autores
A. Ivanov
Department of Chemistry, M. V. Lomonosov Moscow State University
Email: onshornikova@gmail.com
Rússia, Build. 3, 1 Leninskie Gory, Moscow, 119991
S. Filimonov
Department of Chemistry, M. V. Lomonosov Moscow State University
Email: onshornikova@gmail.com
Rússia, Build. 3, 1 Leninskie Gory, Moscow, 119991
O. Shornikova
Department of Chemistry, M. V. Lomonosov Moscow State University
Autor responsável pela correspondência
Email: onshornikova@gmail.com
Rússia, Build. 3, 1 Leninskie Gory, Moscow, 119991
A. Malakho
Institute of New Carbon Materials and Technologies
Email: onshornikova@gmail.com
Rússia, Build. 11, 1 Leninskie Gory, Moscow, 119991