- 作者: Ivanov A.1, Filimonov S.1, Shornikova O.1, Malakho A.2
-
隶属关系:
- Department of Chemistry, M. V. Lomonosov Moscow State University
- Institute of New Carbon Materials and Technologies
- 期: 卷 65, 编号 1 (2016)
- 页面: 282-286
- 栏目: Brief Communications
- URL: https://journals.rcsi.science/1066-5285/article/view/237063
- DOI: https://doi.org/10.1007/s11172-016-1298-y
- ID: 237063
如何引用文章
详细
The composition of gas evolved upon thermal decomposition of individual and carbamidemodified graphite nitrates was determined. The addition of carbamide was shown to result in the 2—4-fold decrease in the content of nitrogen oxides and the 2—5-fold increase in the content of carbon monoxide. The content of nitrogen oxides in the gas phase decreased when the HNO3 : (NH2)2CO molar ratio was equal to 1 : (0.4—1). Combination of carbamide addition with catalytic afterburning provides the 5-fold decrease in the gas-phase amount of nitrogen oxides at the minimum CO content.
作者简介
A. Ivanov
Department of Chemistry, M. V. Lomonosov Moscow State University
Email: onshornikova@gmail.com
俄罗斯联邦, Build. 3, 1 Leninskie Gory, Moscow, 119991
S. Filimonov
Department of Chemistry, M. V. Lomonosov Moscow State University
Email: onshornikova@gmail.com
俄罗斯联邦, Build. 3, 1 Leninskie Gory, Moscow, 119991
O. Shornikova
Department of Chemistry, M. V. Lomonosov Moscow State University
编辑信件的主要联系方式.
Email: onshornikova@gmail.com
俄罗斯联邦, Build. 3, 1 Leninskie Gory, Moscow, 119991
A. Malakho
Institute of New Carbon Materials and Technologies
Email: onshornikova@gmail.com
俄罗斯联邦, Build. 11, 1 Leninskie Gory, Moscow, 119991