A study of the viscosity of hyaluronic acid solutions for the preparation of polyelectrolyte complexes with chitosan
- Autores: Uspenskii S.1, Kil’deeva N.2, Maslova M.2, Demina T.1, Vikhoreva G.2
-
Afiliações:
- N. S. Enikolopov Institute of Synthetic Polymer Materials, Russian Academy of Sciences
- Moscow State University of Design and Technology
- Edição: Volume 65, Nº 1 (2016)
- Páginas: 273-276
- Seção: Full Articles
- URL: https://journals.rcsi.science/1066-5285/article/view/237028
- DOI: https://doi.org/10.1007/s11172-016-1296-0
- ID: 237028
Citar
Resumo
The viscosity of hyaluronic acid solutions kept at different pH values was found to decrease in the following order of pH: 6.5 > 3.5 > 4.3, although acid hydrolysis occurred at a higher rate in the most acidic solution. The poorest stability of the solutions with pH 4.3 was attributed to the compaction of the macromolecules as a result of charge density redistribution along the polyacid chains.
Palavras-chave
Sobre autores
S. Uspenskii
N. S. Enikolopov Institute of Synthetic Polymer Materials, Russian Academy of Sciences
Autor responsável pela correspondência
Email: s.a.uspenskii@mail.ru
Rússia, 70 ul. Profsoyuznaya, Moscow, 117393
N. Kil’deeva
Moscow State University of Design and Technology
Email: s.a.uspenskii@mail.ru
Rússia, 33 ul. Sadovnicheskaya, Moscow, 117997
M. Maslova
Moscow State University of Design and Technology
Email: s.a.uspenskii@mail.ru
Rússia, 33 ul. Sadovnicheskaya, Moscow, 117997
T. Demina
N. S. Enikolopov Institute of Synthetic Polymer Materials, Russian Academy of Sciences
Email: s.a.uspenskii@mail.ru
Rússia, 70 ul. Profsoyuznaya, Moscow, 117393
G. Vikhoreva
Moscow State University of Design and Technology
Email: s.a.uspenskii@mail.ru
Rússia, 33 ul. Sadovnicheskaya, Moscow, 117997