Charge transport in thin layers of ferroelectric Hf0.5Zr0.5O2

Аннотация

The mechanism responsible for the charge transport in thin ferroelectric Hf_0.5Zr_0.5O₂ films has been studied. It is shown that in these films the transport mechanism is phonon-assisted tunneling between the traps. The optimal thickness of dielectric film for TiN/Hf_0.5Zr_0.5O₂/Pt structures is determined. As a result of comparing the experimental current–voltage (I–V) characteristics of TiN/Hf_0.5Zr_0.5O₂/Pt structures with the calculated ones, the thermal and optical energies of the traps are determined and the concentration of the traps is estimated. A comparison between the transport properties of ferroelectric and amorphous Hf_0.5Zr_0.5O₂ films is carried out. It is shown that the charge transport mechanism in this dielectric does not depend on its crystalline phase. A method for decreasing leakage currents in Hf_0.5Zr_0.5O₂ is proposed. A study of the resource of repolarization cycles for TiN/Hf_0.5Zr_0.5O₂/TiN metal-dielectric-metal (MDM) structures fully grown by atomic layer deposition (ALD) has been carried out.