Superhardness effect in transition-metal diborides films


Cite item

Full Text

Open Access Open Access
Restricted Access Access granted
Restricted Access Subscription Access

Abstract

The structure, composition, and properties of transition-metal diboride films have been studied. It was shown that they are characterized by a wide range of structural states, namely from amorphous-like to nanocrystalline with crystallite sizes of 1–50 nm. The characteristic peculiarity of the structure of film transition-metal diborides with high physical and mechanical properties is the formation of a nanocrystalline (columnar) structure with the growth texture in plane [00.1] and a nanocrystallite size of 20–50 nm. The element composition of a superhard highly textured film transition-metal diborides was studied by ion mass spectrometry and Auger electron spectroscopy. The overstoichiometry effect in nanocrystalline transitionmetal diboride films is explained. It was shown that this effect is related to the formation of an additional B⎯B covalent bond, which is realized at subgrain boundaries and leads to the appearance of superhardness in the formed coatings.

About the authors

A. I. Bazhin

Scientific Center of Physical Technologies

Author for correspondence.
Email: algon.61@mail.ru
Ukraine, pl. Svobody 4, Khar’kov, 61077

A. A. Goncharov

Sumy State University

Email: algon.61@mail.ru
Ukraine, ul. Rimskogo-Korsakova 2, Sumy, 40007

A. D. Pogrebnyak

Sumy State University

Email: algon.61@mail.ru
Ukraine, ul. Rimskogo-Korsakova 2, Sumy, 40007

V. A. Stupak

Scientific Center of Physical Technologies

Email: algon.61@mail.ru
Ukraine, pl. Svobody 4, Khar’kov, 61077

S. A. Goncharova

Sumy State University

Email: algon.61@mail.ru
Ukraine, ul. Rimskogo-Korsakova 2, Sumy, 40007

Supplementary files

Supplementary Files
Action
1. JATS XML

Copyright (c) 2016 Pleiades Publishing, Ltd.