Agglomeration and Properties of Ceramics Based on Partially Stabilized Zirconium Dioxide Containing Oxides of Aluminum and Iron


Citar

Texto integral

Acesso aberto Acesso aberto
Acesso é fechado Acesso está concedido
Acesso é fechado Somente assinantes

Resumo

Agglomeration of ceramics of partially stabilized zirconium dioxide containing 5 wt % of aluminum oxide depending on the amount of additive (iron oxide) was studied. It was shown that introduction of an additive promotes a decrease in agglomeration temperature to 1400–1450°С and formation of a dense structure, as well as acquisition of high strength up to 450 MPa (after agglomeration at 1400°С).

Sobre autores

V. Smirnov

Baikov Institute of Metallurgy and Materials Science

Autor responsável pela correspondência
Email: smirnov2007@mail.ru
Rússia, Moscow

T. Obolkina

Baikov Institute of Metallurgy and Materials Science

Email: smirnov2007@mail.ru
Rússia, Moscow

A. Krylov

Baikov Institute of Metallurgy and Materials Science

Email: smirnov2007@mail.ru
Rússia, Moscow

S. Smirnov

Baikov Institute of Metallurgy and Materials Science

Email: smirnov2007@mail.ru
Rússia, Moscow

M. Gol’dberg

Baikov Institute of Metallurgy and Materials Science

Email: smirnov2007@mail.ru
Rússia, Moscow

O. Antonova

Baikov Institute of Metallurgy and Materials Science

Email: smirnov2007@mail.ru
Rússia, Moscow

D. Titov

Baikov Institute of Metallurgy and Materials Science

Email: smirnov2007@mail.ru
Rússia, Moscow

S. Barinov

Baikov Institute of Metallurgy and Materials Science

Email: smirnov2007@mail.ru
Rússia, Moscow

Arquivos suplementares

Arquivos suplementares
Ação
1. JATS XML

Declaração de direitos autorais © Pleiades Publishing, Ltd., 2018