Agglomeration and Properties of Ceramics Based on Partially Stabilized Zirconium Dioxide Containing Oxides of Aluminum and Iron

详细

Agglomeration of ceramics of partially stabilized zirconium dioxide containing 5 wt % of aluminum oxide depending on the amount of additive (iron oxide) was studied. It was shown that introduction of an additive promotes a decrease in agglomeration temperature to 1400–1450°С and formation of a dense structure, as well as acquisition of high strength up to 450 MPa (after agglomeration at 1400°С).