Agglomeration and Properties of Ceramics Based on Partially Stabilized Zirconium Dioxide Containing Oxides of Aluminum and Iron
- Authors: Smirnov V.V.1, Obolkina T.O.1, Krylov A.I.1, Smirnov S.V.1, Gol’dberg M.A.1, Antonova O.S.1, Titov D.D.1, Barinov S.M.1
-
Affiliations:
- Baikov Institute of Metallurgy and Materials Science
- Issue: Vol 9, No 1 (2018)
- Pages: 121-124
- Section: Article
- URL: https://journals.rcsi.science/2075-1133/article/view/207193
- DOI: https://doi.org/10.1134/S2075113318010252
- ID: 207193
Cite item
Abstract
Agglomeration of ceramics of partially stabilized zirconium dioxide containing 5 wt % of aluminum oxide depending on the amount of additive (iron oxide) was studied. It was shown that introduction of an additive promotes a decrease in agglomeration temperature to 1400–1450°С and formation of a dense structure, as well as acquisition of high strength up to 450 MPa (after agglomeration at 1400°С).
Keywords
About the authors
V. V. Smirnov
Baikov Institute of Metallurgy and Materials Science
Author for correspondence.
Email: smirnov2007@mail.ru
Russian Federation, Moscow
T. O. Obolkina
Baikov Institute of Metallurgy and Materials Science
Email: smirnov2007@mail.ru
Russian Federation, Moscow
A. I. Krylov
Baikov Institute of Metallurgy and Materials Science
Email: smirnov2007@mail.ru
Russian Federation, Moscow
S. V. Smirnov
Baikov Institute of Metallurgy and Materials Science
Email: smirnov2007@mail.ru
Russian Federation, Moscow
M. A. Gol’dberg
Baikov Institute of Metallurgy and Materials Science
Email: smirnov2007@mail.ru
Russian Federation, Moscow
O. S. Antonova
Baikov Institute of Metallurgy and Materials Science
Email: smirnov2007@mail.ru
Russian Federation, Moscow
D. D. Titov
Baikov Institute of Metallurgy and Materials Science
Email: smirnov2007@mail.ru
Russian Federation, Moscow
S. M. Barinov
Baikov Institute of Metallurgy and Materials Science
Email: smirnov2007@mail.ru
Russian Federation, Moscow