Composite Ceramic Based on Silicon Carbide

Аннотация

An effective method for preparing dense granular ceramic from SiC with a residual porosity of less than 5.0% is the use of additives of oxide system eutectic compositions. The effect of fine eutectic powder in the Al₂O₃–MnO–SiO₂ system depending on the composition of the charge, compaction pressure and firing temperature on the sintering performance of granular SiC ceramics, is considered. It is established that after firing ceramic at 1250°C with 15 wt.% of eutectic additive, its porosity is 4.2%, and the ultimate strength in bending reaches (95±5) MPa.