Investigation of the Fracture and Strength of a Compound with a Carbide Base of a Wear-Resistant Ion-Plasma Vacuum-Arc Ti–N, Ti–Al–N, Ti–Al–Cr–N, and Ti–Al–Ni–N Coatings by the Scratch Testing

I. V. Blinkov; D. S. Belov; A. O. Volkhonskii; A. V. Chernogor; V. S. Sergevnin; A. P. Demirov

doi:10.3103/S1068366619020028

Investigation of the Fracture and Strength of a Compound with a Carbide Base of a Wear-Resistant Ion-Plasma Vacuum-Arc Ti–N, Ti–Al–N, Ti–Al–Cr–N, and Ti–Al–Ni–N Coatings by the Scratch Testing

Autores: Blinkov I.V.¹, Belov D.S.¹, Volkhonskii A.O.¹, Chernogor A.V.¹, Sergevnin V.S.¹, Demirov A.P.¹
Afiliações:
1. National University of Science and Technology MISiS
Edição: Volume 40, Nº 2 (2019)
Páginas: 171-178
Seção: Article
URL: https://journals.rcsi.science/1068-3666/article/view/229281
DOI: https://doi.org/10.3103/S1068366619020028
ID: 229281

Citar

Texto integral

Acesso aberto
Acesso é fechado

Acesso está concedido
Acesso é fechado

Somente assinantes

Resumo
Sobre autores
Bibliografia
Arquivos suplementares
Estatísticas

Resumo

Comparative studies of the fracture behavior and adhesion strength during scratch testing of a wear-resistant ion-plasma vacuum-arc Ti–N, Ti–Al–N, Ti–Al–Cr–N, and Ti–Al–Ni–N coatings are carried out by the scratch test. The type of failure and the adhesion strength characteristics of the coatings based on L_C1, L_C2, and L_C3 are determined by their structure, by the H³/E ² and H/E parameter values, and by the values of compressive macrostresses.