Electrical and Magnetic Properties of Ultrathin Polycrystalline Fe Films Grown on SiO2/Si(001)
- Авторы: Balashev V.1,2, Ermakov K.2, Chebotkevich L.2, Korobtsov V.1,2
-
Учреждения:
- Institute of Automation and Control Processes, Far Eastern Branch
- School of Natural Sciences
- Выпуск: Том 44, № 7 (2018)
- Страницы: 595-598
- Раздел: Article
- URL: https://journals.rcsi.science/1063-7850/article/view/207783
- DOI: https://doi.org/10.1134/S1063785018070040
- ID: 207783
Цитировать
Аннотация
Ultrathin polycrystalline Fe films have been grown on the oxidized surface of a Si(001) substrate. The resistivity and magnetic hysteresis of Fe films have been measured in the range of thickness from 2.5 to 10 nm. Based on the analysis of the data obtained, it is suggested that there is a transition to the structurally continuous film at a thickness of ~6 nm. It is found that Fe grains in this film acquire the preferred (111) orientation during this transition.
Об авторах
V. Balashev
Institute of Automation and Control Processes, Far Eastern Branch; School of Natural Sciences
Автор, ответственный за переписку.
Email: balashev@mail.dvo.ru
Россия, Vladivostok, 690041; Vladivostok, 690090
K. Ermakov
School of Natural Sciences
Email: balashev@mail.dvo.ru
Россия, Vladivostok, 690090
L. Chebotkevich
School of Natural Sciences
Email: balashev@mail.dvo.ru
Россия, Vladivostok, 690090
V. Korobtsov
Institute of Automation and Control Processes, Far Eastern Branch; School of Natural Sciences
Email: balashev@mail.dvo.ru
Россия, Vladivostok, 690041; Vladivostok, 690090