Specific Features of Microstructure Formation in Co–Cr–Ni–W–Ta Alloys and Their Mechanical Properties
- Authors: Mazalov I.S.1, Suhov D.I.1, Nerush S.V.1, Sulyanova E.A.1
-
Affiliations:
- All-Russian Scientific Research Institute of Aviation Materials
- Issue: Vol 64, No 4 (2019)
- Pages: 575-580
- Section: Real Structure of Crystals
- URL: https://journals.rcsi.science/1063-7745/article/view/194071
- DOI: https://doi.org/10.1134/S106377451904014X
- ID: 194071
Cite item
Abstract
The microstructure and mechanical properties of three experimental compositions of a new heat- and corrosion-resistant cast cobalt-based alloy have been investigated. It is established that compositions are reinforced as a result of the formation of carbide phases in them during aging. It is shown that the ultimate and yield strength of this material at a temperature of 20°C are, respectively, 650(50) and 440(10) MPa. An analysis of the heat resistance of alloy samples has revealed that they withstand loads of 170 MPa (for 329 h) and 25 MPa (for 1093 h) at temperatures of 800 and 1100°C, respectively. The mechanical properties of the new alloy are superior of those of the foreign heat-resistant alloy FSX-414.
About the authors
I. S. Mazalov
All-Russian Scientific Research Institute of Aviation Materials
Email: sulyanova@gmail.com
Russian Federation, Moscow, 105005
D. I. Suhov
All-Russian Scientific Research Institute of Aviation Materials
Email: sulyanova@gmail.com
Russian Federation, Moscow, 105005
S. V. Nerush
All-Russian Scientific Research Institute of Aviation Materials
Email: sulyanova@gmail.com
Russian Federation, Moscow, 105005
E. A. Sulyanova
All-Russian Scientific Research Institute of Aviation Materials
Author for correspondence.
Email: sulyanova@gmail.com
Russian Federation, Moscow, 105005
Supplementary files