Formation of a Nickel–Aluminum Intermetallic during Ion-Beam Mixing

V. L. Vorob’ev; I. N. Klimova; A. A. Kolotov; P. V. Bykov; V. Ya. Bayankin

doi:10.1134/S1027451019060569

Formation of a Nickel–Aluminum Intermetallic during Ion-Beam Mixing

作者: Vorob’ev V.L.¹, Klimova I.N.¹, Kolotov A.A.¹, Bykov P.V.¹, Bayankin V.Y.¹
隶属关系:
1. Udmurt Federal Research Center, Ural Branch, Russian Academy of Sciences
期: 卷 13, 编号 6 (2019)
页面: 1225-1229
栏目: Article
URL: https://journals.rcsi.science/1027-4510/article/view/196554
DOI: https://doi.org/10.1134/S1027451019060569
ID: 196554

如何引用文章

全文:

开放存取

##reader.subscriptionAccessGranted##
受限制的访问

订阅存取

详细
作者简介
参考
补充文件
统计

详细

The results of studying the X-ray photoelectron spectroscopy of the chemical composition of nickel surface layers with a deposited aluminum film, depending on the dose of irradiation with argon ions, are presented. Analysis of the spectra shows the formation of Ni₃Al aluminide during ion-beam mixing. The highest content (~20%) of this compound in the modified layer is observed at an implantation dose of 5 × 10¹⁶ cm^–2.