Calcium Phosphate Foam Ceramic Based on Hydroxyapatite–Brushite Powder Mixture

详细

The introduction of 10 – 50% (by weight) brushite powder, preheated at 50° and then fired at 1200°C, into a permeating suspension based on hydroxyapatite powder heat-treated at 800°C results in partial decomposition of hydroxyapatite to the α- and β-modifications of tricalcium phosphate. The presence of a tricalcium phosphate phase in calcium phosphate foam ceramic promotes an increase of the porosity from 40 to 60% and the resorption with significant static strength reduction from 3 – 7 to 0.3 MPa.