Changes in the Specific Heat of U8 Steel after Quenching by Deforming Cutting during Its Heating to 400°C
- 作者: Simonov V.1, Zubkov N.1, Degtyareva A.1, Vasil’ev S.1
-
隶属关系:
- Bauman Moscow State Technical University
- 期: 卷 2019, 编号 6 (2019)
- 页面: 624-628
- 栏目: Hardening and Coating Technologies
- URL: https://journals.rcsi.science/0036-0295/article/view/173297
- DOI: https://doi.org/10.1134/S0036029519060168
- ID: 173297
如何引用文章
详细
The specific heat of U8 steel is measured after deforming cutting, quenching from furnace heating into water, and subsequent heating in a calorimeter in the temperature range 100–400°C. The temperature dependences of the specific heat after deforming cutting and furnace quenching have substantially different characters, which is due to a nonequilibrium state of the structure in the material after quenching by deforming cutting. The change in the enthalpy of U8 steel during its heating for these types of quenching is calculated.
作者简介
V. Simonov
Bauman Moscow State Technical University
编辑信件的主要联系方式.
Email: dega_70@mail.ru
俄罗斯联邦, Moscow, 105005
N. Zubkov
Bauman Moscow State Technical University
Email: dega_70@mail.ru
俄罗斯联邦, Moscow, 105005
A. Degtyareva
Bauman Moscow State Technical University
Email: dega_70@mail.ru
俄罗斯联邦, Moscow, 105005
S. Vasil’ev
Bauman Moscow State Technical University
Email: dega_70@mail.ru
俄罗斯联邦, Moscow, 105005
![](/img/style/loading.gif)