Changes in the Specific Heat of U8 Steel after Quenching by Deforming Cutting during Its Heating to 400°C
- Авторы: Simonov V.1, Zubkov N.1, Degtyareva A.1, Vasil’ev S.1
-
Учреждения:
- Bauman Moscow State Technical University
- Выпуск: Том 2019, № 6 (2019)
- Страницы: 624-628
- Раздел: Hardening and Coating Technologies
- URL: https://journals.rcsi.science/0036-0295/article/view/173297
- DOI: https://doi.org/10.1134/S0036029519060168
- ID: 173297
Цитировать
Аннотация
The specific heat of U8 steel is measured after deforming cutting, quenching from furnace heating into water, and subsequent heating in a calorimeter in the temperature range 100–400°C. The temperature dependences of the specific heat after deforming cutting and furnace quenching have substantially different characters, which is due to a nonequilibrium state of the structure in the material after quenching by deforming cutting. The change in the enthalpy of U8 steel during its heating for these types of quenching is calculated.
Ключевые слова
Об авторах
V. Simonov
Bauman Moscow State Technical University
Автор, ответственный за переписку.
Email: dega_70@mail.ru
Россия, Moscow, 105005
N. Zubkov
Bauman Moscow State Technical University
Email: dega_70@mail.ru
Россия, Moscow, 105005
A. Degtyareva
Bauman Moscow State Technical University
Email: dega_70@mail.ru
Россия, Moscow, 105005
S. Vasil’ev
Bauman Moscow State Technical University
Email: dega_70@mail.ru
Россия, Moscow, 105005
![](/img/style/loading.gif)