Changes in the Specific Heat of U8 Steel after Quenching by Deforming Cutting during Its Heating to 400°C
- Autores: Simonov V.1, Zubkov N.1, Degtyareva A.1, Vasil’ev S.1
-
Afiliações:
- Bauman Moscow State Technical University
- Edição: Volume 2019, Nº 6 (2019)
- Páginas: 624-628
- Seção: Hardening and Coating Technologies
- URL: https://journals.rcsi.science/0036-0295/article/view/173297
- DOI: https://doi.org/10.1134/S0036029519060168
- ID: 173297
Citar
Resumo
The specific heat of U8 steel is measured after deforming cutting, quenching from furnace heating into water, and subsequent heating in a calorimeter in the temperature range 100–400°C. The temperature dependences of the specific heat after deforming cutting and furnace quenching have substantially different characters, which is due to a nonequilibrium state of the structure in the material after quenching by deforming cutting. The change in the enthalpy of U8 steel during its heating for these types of quenching is calculated.
Palavras-chave
Sobre autores
V. Simonov
Bauman Moscow State Technical University
Autor responsável pela correspondência
Email: dega_70@mail.ru
Rússia, Moscow, 105005
N. Zubkov
Bauman Moscow State Technical University
Email: dega_70@mail.ru
Rússia, Moscow, 105005
A. Degtyareva
Bauman Moscow State Technical University
Email: dega_70@mail.ru
Rússia, Moscow, 105005
S. Vasil’ev
Bauman Moscow State Technical University
Email: dega_70@mail.ru
Rússia, Moscow, 105005
![](/img/style/loading.gif)