Changes in the Specific Heat of U8 Steel after Quenching by Deforming Cutting during Its Heating to 400°C
- Авторлар: Simonov V.1, Zubkov N.1, Degtyareva A.1, Vasil’ev S.1
-
Мекемелер:
- Bauman Moscow State Technical University
- Шығарылым: Том 2019, № 6 (2019)
- Беттер: 624-628
- Бөлім: Hardening and Coating Technologies
- URL: https://journals.rcsi.science/0036-0295/article/view/173297
- DOI: https://doi.org/10.1134/S0036029519060168
- ID: 173297
Дәйексөз келтіру
Аннотация
The specific heat of U8 steel is measured after deforming cutting, quenching from furnace heating into water, and subsequent heating in a calorimeter in the temperature range 100–400°C. The temperature dependences of the specific heat after deforming cutting and furnace quenching have substantially different characters, which is due to a nonequilibrium state of the structure in the material after quenching by deforming cutting. The change in the enthalpy of U8 steel during its heating for these types of quenching is calculated.
Негізгі сөздер
Авторлар туралы
V. Simonov
Bauman Moscow State Technical University
Хат алмасуға жауапты Автор.
Email: dega_70@mail.ru
Ресей, Moscow, 105005
N. Zubkov
Bauman Moscow State Technical University
Email: dega_70@mail.ru
Ресей, Moscow, 105005
A. Degtyareva
Bauman Moscow State Technical University
Email: dega_70@mail.ru
Ресей, Moscow, 105005
S. Vasil’ev
Bauman Moscow State Technical University
Email: dega_70@mail.ru
Ресей, Moscow, 105005
![](/img/style/loading.gif)