Acoustic emission analysis of the stages of deformation of TRIP steel

Resumo

The kinetics of damage accumulation and deformation martensite formation in cold-rolled austenitic–martensitic VNS9-Sh TRIP steel during static tension at room temperature is studied at various stages of plastic deformation and fracture by acoustic emission and X-ray diffraction. The threshold stresses that correspond to the beginning of dislocation motion and intense dislocation generation predominantly in surface layers are determined. Deformation martensite is shown to form after a yield plateau and its formation is most intensely at the stage of strain hardening.