Acoustic emission analysis of the stages of deformation of TRIP steel
- 作者: Penkin A.1, Terent’ev V.2, Roshchupkin V.2, Slizov A.3, Sirotinkin V.2
-
隶属关系:
- ZAO Special Diagnostic Systems
- Baikov Institute of Metallurgy and Materials Science
- OAO Kamov
- 期: 卷 2017, 编号 4 (2017)
- 页面: 306-311
- 栏目: Applied Problems of Strength and Plasticity
- URL: https://journals.rcsi.science/0036-0295/article/view/171437
- DOI: https://doi.org/10.1134/S003602951704019X
- ID: 171437
如何引用文章
详细
The kinetics of damage accumulation and deformation martensite formation in cold-rolled austenitic–martensitic VNS9-Sh TRIP steel during static tension at room temperature is studied at various stages of plastic deformation and fracture by acoustic emission and X-ray diffraction. The threshold stresses that correspond to the beginning of dislocation motion and intense dislocation generation predominantly in surface layers are determined. Deformation martensite is shown to form after a yield plateau and its formation is most intensely at the stage of strain hardening.
作者简介
A. Penkin
ZAO Special Diagnostic Systems
Email: fatig@mail.ru
俄罗斯联邦, Moscow, 119991
V. Terent’ev
Baikov Institute of Metallurgy and Materials Science
编辑信件的主要联系方式.
Email: fatig@mail.ru
俄罗斯联邦, Leninskii pr. 49, Moscow, 119991
V. Roshchupkin
Baikov Institute of Metallurgy and Materials Science
Email: fatig@mail.ru
俄罗斯联邦, Leninskii pr. 49, Moscow, 119991
A. Slizov
OAO Kamov
Email: fatig@mail.ru
俄罗斯联邦, Lyubertsy, Moscow oblast, 140007
V. Sirotinkin
Baikov Institute of Metallurgy and Materials Science
Email: fatig@mail.ru
俄罗斯联邦, Leninskii pr. 49, Moscow, 119991
![](/img/style/loading.gif)