Отправить статью по E-mail Analysis of Phase Transformations of Supercooled Austenite in Low-Alloy Steel with Boron Additives
- Авторы: Łętkowska B.1, Dziurka R.2, Bała P.2
-
Учреждения:
- Department of Materials Science, Welding and Strength of Materials, Wrocław University of Technology
- Department of Physical and Powder Metallurgy, AGH University of Science and Technology
- Выпуск: Том 57, № 9-10 (2016)
- Страницы: 525-530
- Раздел: Article
- URL: https://journals.rcsi.science/0026-0673/article/view/235143
- DOI: https://doi.org/10.1007/s11041-016-9916-8
- ID: 235143
Цитировать
Открытый доступ
Доступ предоставлен
Только для подписчиков
Аннотация
Adiagram of transformations in low-alloy boron-containing steel B27 with high resistance to abrasive wear is plotted under continuous cooling. Chemical, metallographic and dilatometric analyses are performed, and the hardness of the steel is measured. Continuous cooling curves are obtained from the temperature of austenitization at a rate of 0.17 – 25 K/sec in the temperature range of 800 – 500°C.
Об авторах
B. Łętkowska
Department of Materials Science, Welding and Strength of Materials, Wrocław University of Technology
Email: petroprom2013@yandex.ru
Польша, Wroclaw
R. Dziurka
Department of Physical and Powder Metallurgy, AGH University of Science and Technology
Email: petroprom2013@yandex.ru
Польша, Krakow
P. Bała
Department of Physical and Powder Metallurgy, AGH University of Science and Technology
Email: petroprom2013@yandex.ru
Польша, Krakow
Дополнительные файлы