Primary Recrystallization Texture in FCC-Metal with Low Packing Defect Energy
- Авторлар: Zorina M.A.1, Lobanov M.L.1, Makarova E.A.1, Rusakov G.M.1,2
-
Мекемелер:
- B. N. El’tsin Ural Federal University
- Institue of Metals, Ural Section, Russian Academy of Sciences
- Шығарылым: Том 60, № 5-6 (2018)
- Беттер: 329-336
- Бөлім: Article
- URL: https://journals.rcsi.science/0026-0673/article/view/236357
- DOI: https://doi.org/10.1007/s11041-018-0280-8
- ID: 236357
Дәйексөз келтіру
Аннотация
The method of orientation microscopy (EBSD) is used to study the special features of recrystallization texture in drawn copper wire. It is shown that the strict crystallographic relationships between deformation and recrystallization orientations are consequences of the dominant role in structural transformations of special misorientations, i.e. special boundaries. Mechanisms of the appearance and “growth” of annealing twins are proposed.
Авторлар туралы
M. Zorina
B. N. El’tsin Ural Federal University
Email: m.l.lobanov@urfu.ru
Ресей, Ekaterinburg
M. Lobanov
B. N. El’tsin Ural Federal University
Хат алмасуға жауапты Автор.
Email: m.l.lobanov@urfu.ru
Ресей, Ekaterinburg
E. Makarova
B. N. El’tsin Ural Federal University
Email: m.l.lobanov@urfu.ru
Ресей, Ekaterinburg
G. Rusakov
B. N. El’tsin Ural Federal University; Institue of Metals, Ural Section, Russian Academy of Sciences
Email: m.l.lobanov@urfu.ru
Ресей, Ekaterinburg; Ekaterinburg
Қосымша файлдар