Email this article Primary Recrystallization Texture in FCC-Metal with Low Packing Defect Energy
- Authors: Zorina M.A.1, Lobanov M.L.1, Makarova E.A.1, Rusakov G.M.1,2
-
Affiliations:
- B. N. El’tsin Ural Federal University
- Institue of Metals, Ural Section, Russian Academy of Sciences
- Issue: Vol 60, No 5-6 (2018)
- Pages: 329-336
- Section: Article
- URL: https://journals.rcsi.science/0026-0673/article/view/236357
- DOI: https://doi.org/10.1007/s11041-018-0280-8
- ID: 236357
Cite item
Open Access
Access granted
Subscription Access
Abstract
The method of orientation microscopy (EBSD) is used to study the special features of recrystallization texture in drawn copper wire. It is shown that the strict crystallographic relationships between deformation and recrystallization orientations are consequences of the dominant role in structural transformations of special misorientations, i.e. special boundaries. Mechanisms of the appearance and “growth” of annealing twins are proposed.
About the authors
M. A. Zorina
B. N. El’tsin Ural Federal University
Email: m.l.lobanov@urfu.ru
Russian Federation, Ekaterinburg
M. L. Lobanov
B. N. El’tsin Ural Federal University
Author for correspondence.
Email: m.l.lobanov@urfu.ru
Russian Federation, Ekaterinburg
E. A. Makarova
B. N. El’tsin Ural Federal University
Email: m.l.lobanov@urfu.ru
Russian Federation, Ekaterinburg
G. M. Rusakov
B. N. El’tsin Ural Federal University; Institue of Metals, Ural Section, Russian Academy of Sciences
Email: m.l.lobanov@urfu.ru
Russian Federation, Ekaterinburg; Ekaterinburg
Supplementary files