Growth of Y3Fe5O12 films on Si with AlOx and SiO2 buffer layers by ion beam sputtering

Аннотация

Amorphous yttrium iron garnet films ranging in thickness from 100 to 600 nm have been produced on single-crystal silicon substrates by sputtering a polycrystalline target with the composition Y₃Fe₅O₁₂ (yttrium iron garnet) by a mixture of argon and oxygen ions. Before film growth, AlO_x or SiO₂ buffer layers up to 0.8 μm in thickness were grown on the Si surface. The heterostructures were crystallized by annealing in air at a temperature of 950°C for 30 min. The properties of the films were studied by magneto-optical techniques, using Kerr effect and ferromagnetic resonance measurements. The Gilbert damping parameter reached 2.8 × 10^–3 and the effective planar magnetic anisotropy field was independent of the nature of the buffer layer. This suggests that the thin-film heterostructures obtained in this study are potentially attractive for use in spin-wave semiconductor devices.