Structure and Mechanical Properties of TiAlSiY Vacuum-Arc Coatings Deposited in Nitrogen Atmosphere

Авторы: Beresnev V.M.¹, Sobol O.V.², Pogrebnjak A.D.³, Lytovchenko S.V.¹, Klimenko S.A.⁴, Stolbovoy V.A.⁵, Srebniuk P.A.¹, Manokhin A.S.⁴, Kovaleva M.G.⁶, Novikov V.Y.⁶, Meilekhov A.A.², Nyemchenko U.S.¹, Barmin A.E.², Turbin P.V.¹^,7
Учреждения:
1. V.N. Karazin Kharkiv National University
2. National Technical University Kharkiv Technical Institute
3. Sumy State University
4. Bakul Institute for Superhard Materials
5. National Scientific Center Kharkiv Institute of Physics and Technology
6. Belgorod State National Research University
7. Science Center of Physics and Technology
Выпуск: Том 9, № 3 (2018)
Страницы: 410-417
Раздел: Functional Coatings and Surface Treatment
URL: https://journals.rcsi.science/2075-1133/article/view/207409
DOI: https://doi.org/10.1134/S2075113318030073
ID: 207409

Цитировать

Полный текст

Открытый доступ
Доступ закрыт

Доступ предоставлен
Доступ закрыт

Только для подписчиков

Аннотация
Об авторах
Список литературы
Дополнительные файлы
Статистика

Аннотация

The effect of a negative bias potential applied to the substrate on elemental composition, structure, and mechanical properties of vacuum-arc TiAlSiY nitride coatings is investigated by different methods. It is ascertained that applying a high (up to–500 V) bias voltage leads to a selective sputtering of target as well as significant microdeformation of the coating, small-sized growth of crystallites, and their preferred orientation along the [110] direction. In this case, the coating deposited has a low hardness H = 6.95 GPa and propensity to intense wear under scratch and tribological tests. Crystallites with stoichiometric composition ~140 nm in size and [111] preferred orientation perpendicular to the surface of growth are formed at the bias potential about–200 V, and superhard (H = 49.5 GPa) and wear-resistant coatings are grown under such conditions. The mechanisms of formation of the structure of multielement coatings are discussed. It is shown that formation of an amorphous phase and nanocrystal [110] texture takes place at a high bias potential owing to the process of radiation-stimulated selective spraying of the target. Formation of microstrained crystallites 10 nm in size caused by the weakening of interatomic bonds is observed in the coating under such deposition conditions, and it leads to the decrease in coating hardness and fast destruction during tribological testing. Substantial bias voltage dependence of deposited coating properties is established in our investigations.

Ключевые слова

vacuum-arc deposition, wear, friction coefficient, surface, structural engineering, solid solution

Дополнительные файлы

Доп. файлы

Действие

1. JATS XML

Скачать

Имя пользователя
Пароль
Запомнить меня

Забыли пароль?	Регистрация

Имя пользователя
Пароль
Запомнить меня

Забыли пароль?	Регистрация

Structure and Mechanical Properties of TiAlSiY Vacuum-Arc Coatings Deposited in Nitrogen Atmosphere

Полный текст

Аннотация

Ключевые слова

Об авторах

V. Beresnev

O. Sobol

A. Pogrebnjak

S. Lytovchenko

S. Klimenko

V. Stolbovoy

P. Srebniuk

A. Manokhin

M. Kovaleva

V. Novikov

A. Meilekhov

U. Nyemchenko

A. Barmin

P. Turbin

Дополнительные файлы