Effect of the grain size on accumulation of scalar density of dislocations and its components in low-alloy Cu–Al
- Authors: Koneva N.A.1, Trishkina L.I.1, Cherkasova T.V.1,2, Kozlov E.V.1
-
Affiliations:
- Tomsk State University of Architecture and Building
- Tomsk Polytechnic University
- Issue: Vol 8, No 4 (2017)
- Pages: 566-572
- Section: Article
- URL: https://journals.rcsi.science/2075-1133/article/view/206642
- DOI: https://doi.org/10.1134/S207511331704013X
- ID: 206642
Cite item
Abstract
The dislocation structure of deformed polycrystal Cu–Al alloys was studied by the TEM method. Measurement and separation of the scalar densities (〈ρ〉) by components were carried out: density (ρG) of the geometrically necessary dislocations (GND) and density (ρS) of the statistically stored dislocations (SSD). Effect of the grain size on the GND and SSD accumulation was established.
Keywords
About the authors
N. A. Koneva
Tomsk State University of Architecture and Building
Author for correspondence.
Email: koneva@tsuab.ru
Russian Federation, Tomsk, 634003
L. I. Trishkina
Tomsk State University of Architecture and Building
Email: koneva@tsuab.ru
Russian Federation, Tomsk, 634003
T. V. Cherkasova
Tomsk State University of Architecture and Building; Tomsk Polytechnic University
Email: koneva@tsuab.ru
Russian Federation, Tomsk, 634003; Tomsk, 634050
E. V. Kozlov
Tomsk State University of Architecture and Building
Email: koneva@tsuab.ru
Russian Federation, Tomsk, 634003