Interdiffusion in lithium–lead melts

R. A. Khairulin; S. V. Stankus; R. N. Abdullaev

doi:10.1134/S0869864317050122

Interdiffusion in lithium–lead melts

作者: Khairulin R.A.¹, Stankus S.V.¹, Abdullaev R.N.²
隶属关系:
1. Kutateladze Institute of Thermophysics SB RAS
2. Novosibirsk State University
期: 卷 24, 编号 5 (2017)
页面: 773-778
栏目: Article
URL: https://journals.rcsi.science/1531-8699/article/view/217104
DOI: https://doi.org/10.1134/S0869864317050122
ID: 217104

如何引用文章

全文:

开放存取

##reader.subscriptionAccessGranted##
受限制的访问

订阅存取

详细
作者简介
参考
补充文件
统计

详细

Interdiffusion in lithium-lead melts containing 10.0, 15.0, 18.1, 20.0, 25.1, 30.2, 38.2, 40.1, 43.1, 46.7, 50.2, 60.2, and 70.0 at. % Pb was investigated using gamma-ray attenuation technique in the temperature range from 720 to 1030 K. It has been found that the concentration dependence of the interdiffusion coefficient has a maximum in the vicinity of 20 at. % Pb. This phenomenon is shown to relate to a tendency of formation of short-range order in liquid alloys of lithium−lead.