Отправить статью по E-mail Change of the thermal behavior of 55Bi2O3 ⋅ 45B2O3 glass at annealing close to the vitrification temperature
- Авторы: Babitskii N.A.1, Zhereb V.P.1, Bermeshev T.V.1
-
Учреждения:
- Siberian Federal University
- Выпуск: Том 42, № 2 (2016)
- Страницы: 149-153
- Раздел: Article
- URL: https://journals.rcsi.science/1087-6596/article/view/215357
- DOI: https://doi.org/10.1134/S1087659616020024
- ID: 215357
Цитировать
Открытый доступ
Доступ предоставлен
Только для подписчиков
Аннотация
The characteristic properties of relaxation processes for 55Bi2O3 ⋅ 45B2O3 glass were described. The pattern of changes of the vitrification temperature (Tg) is found to be quasi-periodic; the value of the endothermic effect near Tg (ΔC’p) and the difference between the softening point and the vitrification temperature (Tm–Tg) were determined. The temperature-time parameters of the transition from quasi-periodic to the continuous change of the properties were determined and an explanation of such behavior of the system was offered.
Ключевые слова
Об авторах
N. Babitskii
Siberian Federal University
Автор, ответственный за переписку.
Email: irbis_btv@mail.ru
Россия, pr. Svobodny 79, Krasnoyarsk, 660041
V. Zhereb
Siberian Federal University
Email: irbis_btv@mail.ru
Россия, pr. Svobodny 79, Krasnoyarsk, 660041
T. Bermeshev
Siberian Federal University
Email: irbis_btv@mail.ru
Россия, pr. Svobodny 79, Krasnoyarsk, 660041
Дополнительные файлы