Email this article Change of the thermal behavior of 55Bi2O3 ⋅ 45B2O3 glass at annealing close to the vitrification temperature
- Authors: Babitskii N.A.1, Zhereb V.P.1, Bermeshev T.V.1
-
Affiliations:
- Siberian Federal University
- Issue: Vol 42, No 2 (2016)
- Pages: 149-153
- Section: Article
- URL: https://journals.rcsi.science/1087-6596/article/view/215357
- DOI: https://doi.org/10.1134/S1087659616020024
- ID: 215357
Cite item
Open Access
Access granted
Subscription Access
Abstract
The characteristic properties of relaxation processes for 55Bi2O3 ⋅ 45B2O3 glass were described. The pattern of changes of the vitrification temperature (Tg) is found to be quasi-periodic; the value of the endothermic effect near Tg (ΔC’p) and the difference between the softening point and the vitrification temperature (Tm–Tg) were determined. The temperature-time parameters of the transition from quasi-periodic to the continuous change of the properties were determined and an explanation of such behavior of the system was offered.
Keywords
About the authors
N. A. Babitskii
Siberian Federal University
Author for correspondence.
Email: irbis_btv@mail.ru
Russian Federation, pr. Svobodny 79, Krasnoyarsk, 660041
V. P. Zhereb
Siberian Federal University
Email: irbis_btv@mail.ru
Russian Federation, pr. Svobodny 79, Krasnoyarsk, 660041
T. V. Bermeshev
Siberian Federal University
Email: irbis_btv@mail.ru
Russian Federation, pr. Svobodny 79, Krasnoyarsk, 660041
Supplementary files