Combined Carbothermal Synthesis of Powders in the B4C–SiC–TiB2 System
- Authors: Kotsar’ T.V.1, Danilovich D.P.1, Ordan’yan S.S.1, Vikhman S.V.1
-
Affiliations:
- St. Petersburg State Technological Institute (Technical University)
- Issue: Vol 58, No 2 (2017)
- Pages: 174-178
- Section: Article
- URL: https://journals.rcsi.science/1083-4877/article/view/248811
- DOI: https://doi.org/10.1007/s11148-017-0076-1
- ID: 248811
Cite item
Abstract
A mixture of boric acid, silicon dioxide, and titanium dioxide powders in the eutectic ratio was reduced by carbon (as soot) at 1600°C in vacuo in order to produce phases in the B4C–SiC–TiB2 system. Only the expected phases were identified in the synthesis products. The synthesized powders were boron carbide crystals ìm in size and nanoparticles.
About the authors
T. V. Kotsar’
St. Petersburg State Technological Institute (Technical University)
Author for correspondence.
Email: asid-92@mail.ru
Russian Federation, St. Petersburg
D. P. Danilovich
St. Petersburg State Technological Institute (Technical University)
Email: asid-92@mail.ru
Russian Federation, St. Petersburg
S. S. Ordan’yan
St. Petersburg State Technological Institute (Technical University)
Email: asid-92@mail.ru
Russian Federation, St. Petersburg
S. V. Vikhman
St. Petersburg State Technological Institute (Technical University)
Email: asid-92@mail.ru
Russian Federation, St. Petersburg
Supplementary files