Effect of inhibitors on carbon steel corrosion in foaming solutions
- Авторы: Kostyaev A.1, Balmasov A.2, Inasaridze L.2
-
Учреждения:
- Ivanovo Institute of State Fire Fighting Service of the Ministry of Russian Federation for Civil Defense, Emergencies, and Elimination of the Consequences of Natural Disasters
- Ivanovo State University of Chemistry and Technology
- Выпуск: Том 86, № 2 (2016)
- Страницы: 429-433
- Раздел: Supplement: Rossiiskii Khimicheskii Zhurnal–Zhurnal Rossiiskogo Khimicheskogo Obshchestva im. D.I. Mendeleeva (Russian Chemistry Journal)
- URL: https://journals.rcsi.science/1070-3632/article/view/214072
- DOI: https://doi.org/10.1134/S1070363216020420
- ID: 214072
Цитировать
Аннотация
The corrosion behavior of carbon steel in PO-6TS-M foaming solution was studied. Several kinds of inhibiting additives were tested for their ability to reduce the corrosion rate of steel. The antipyrene additive to the foaming solution was shown to be the most effective in reducing corrosion rate of carbon steel. The optimum concentration of the inhibitor additive was determined.
Ключевые слова
Об авторах
A. Kostyaev
Ivanovo Institute of State Fire Fighting Service of the Ministry of Russian Federation for Civil Defense, Emergencies, and Elimination of the Consequences of Natural Disasters
Автор, ответственный за переписку.
Email: k87aa@mail.ru
Россия, pr. Stroitelei 33, Ivanovo, 153040
A. Balmasov
Ivanovo State University of Chemistry and Technology
Email: k87aa@mail.ru
Россия, Sheremetevskii pr. 7, Ivanovo, 153000
L. Inasaridze
Ivanovo State University of Chemistry and Technology
Email: k87aa@mail.ru
Россия, Sheremetevskii pr. 7, Ivanovo, 153000