Dispersion and phase transformations of intermetallic compounds and alloys of Ti, Zr, and Y with iron and nickel in the reaction with ammonia


如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅存取

详细

The review collates the results of studies on the chemical dispersion and phase transformations of Ti, Zr, and Y alloys with iron and nickel during the reaction with ammonia at a pressure of 0.6—0.8 MPa in the temperature range of 100—500 °C in the presence of NH4Cl as the activator. Promising working materials for metal hydride hydrogen storage, including alloys (Ti90Mg10, Y67Fe33, and Ti67Fe33) and intermetallics (Ti2Ni, Zr2Ni, Zr3Al2, ZrV2), are considered. At 150—250 °C, the mentioned intermetallics absorb considerable amounts of hydrogen with conservation of the initial metallic lattice and formation of the highly dispersed hydrides Ti2NiH3.3, Zr2NiH4.7, Zr3Al2H1.1, and ZrV2H2.2. The phase transformations taking place on heating of the intermetallics from 250 to 500 °C, resulting in mixtures of intermetallic hydridonitrides and metal nitrides, are elucidated. The transformation products of the Ti90Mg10, Y67Fe33, and Ti67Fe33 alloys in ammonia atmosphere in the temperature range of 100—500 °C are established.

作者简介

B. Tarasov

Institute of Problems of Chemical Physics, Russian Academy of Sciences

Email: fvn@icp.ac.ru
俄罗斯联邦, 1 prosp. Akad. Semenova, Chernogolovka, Moscow Region, 142432

E. Fokina

Institute of Problems of Chemical Physics, Russian Academy of Sciences

Email: fvn@icp.ac.ru
俄罗斯联邦, 1 prosp. Akad. Semenova, Chernogolovka, Moscow Region, 142432

V. Fokin

Institute of Problems of Chemical Physics, Russian Academy of Sciences

编辑信件的主要联系方式.
Email: fvn@icp.ac.ru
俄罗斯联邦, 1 prosp. Akad. Semenova, Chernogolovka, Moscow Region, 142432

补充文件

附件文件
动作
1. JATS XML

版权所有 © Springer Science+Business Media New York, 2016