Low Temperature Magnetic Properties of Amorphous Ferromagnetic Fe–Si–B Glass-Coated and Glass Removed Microwire

Аннотация

This work presents results of investigations of low temperature magnetic properties of microwires, fabricated by the Ulitovsky–Taylor method from Fe–Si–B alloy. Influence of the glass coating presence on the magnetostatic properties was shown at room temperature and at 2 K. Conclusions about the peculiarities of temperature dependence of the magnetic moment, measured in low and high magnetic fields (10 Oe–5 kOe) in the temperature range from 2 to 300 K for a sample with partially reduced fabricated processinduced stress by removing the glass, were made.