Evolution of the vanadium pentoxide V2O5 crystal surface after vacuum annealing

详细

A complex study of the (001) cleavage surface of a V₂O₅ single crystal annealed in vacuum at 450 and 550°C has been performed. Tunnel microscopy of the sample surface annealed in vacuum at 550°C showed the formation of a plane with a corundum structure, reconstructed according to the V₂O₃ (0001)-(1/√3 × 1/√3)R30° type, on the surface. X-ray photoelectron spectroscopy revealed a significant modification of interatomic bonds in the surface layers of V₂O₅ single crystal after vacuum annealing at 550°C, which is related to the partial reduction of V⁵⁺ ions and formation of lower vanadium oxides. These modifications lead to a decrease in the electrical resistivity of V₂O₅ and the occurrence of bending at a temperature of 61.5°С in the temperature dependence of the sample resistance, which is indicative of phase transition.