Nano-Scratching resistance of high-chromium white cast iron and its correlation with wear of cBN tool in machining


Дәйексөз келтіру

Толық мәтін

Ашық рұқсат Ашық рұқсат
Рұқсат жабық Рұқсат берілді
Рұқсат жабық Тек жазылушылар үшін

Аннотация

In this paper, a nano-scratch testing approach was used to measure and evaluate the abrasion wear resistance of high-chromium white cast irons in order to understand the wear mechanism in the interaction between the high-chromium white cast iron and the cBN cutting tool during the machining process. Scratch testing was performed on a nanoindentation instrument using a diamond indenter as the scratch tool. Linear multi-pass scratches in the same path were made on pre-worn surfaces of test materials. The correlation of the scratching resistance and tool wear measured from the machining is presented by the flank wear and maximum scratch depth. The appearance of the cutting edge on a cBN tool suggests that the abrasion wear is mainly related with a combined effect of the carbides and the matrix during machining the high-chromium white cast iron.

Авторлар туралы

L. Chen

School of manufacturing science and engineering

Хат алмасуға жауапты Автор.
Email: chenlingscu@scu.edu.cn
ҚХР, Chengdu, 610065

J. Persson

Division of production and materials engineering

Email: chenlingscu@scu.edu.cn
Швеция, Lund

J. Ståhl

Division of production and materials engineering

Email: chenlingscu@scu.edu.cn
Швеция, Lund

J. Zhou

Division of production and materials engineering

Email: chenlingscu@scu.edu.cn
Швеция, Lund

Қосымша файлдар

Қосымша файлдар
Әрекет
1. JATS XML

© Allerton Press, Inc., 2017