Structural and Dielectric Properties of Lead-Free Zr-Doped Barium Titanates
- Autores: Vasawade S.D.1, Paramaje S.S.1, Choudhari N.J.2, Grampurohit B.V.1, Rendale M.K.2, Mathad S.N.2, Hiremath C.S.1, Pujar R.B.1
-
Afiliações:
- Department of PG Studies in Physics
- Department of Physics
- Edição: Volume 27, Nº 1 (2018)
- Páginas: 26-32
- Seção: Article
- URL: https://journals.rcsi.science/1061-3862/article/view/195892
- DOI: https://doi.org/10.3103/S1061386218010119
- ID: 195892
Citar
Resumo
Lead-free BaZrxTi1–xO3 ferroelectrics (x = 0.2, 0.4, 0.6, 0.8) were synthesized by conventional double-sintering technique. The structural, morphological, and dielectric properties of BaZrxTi1–xO3 were investigated as a function of zirconium content x. A single-phase perovskite structure of tetragonal ceramics was identified by XRD. The SEM images of the ferroelectrics exhibit fine grains of varied porosity. All synthesized samples exhibited dielectric dispersion at low frequencies.
Palavras-chave
Sobre autores
S. Vasawade
Department of PG Studies in Physics
Email: mkrendale@gmail.com
Índia, Hubballi, Karnataka
S. Paramaje
Department of PG Studies in Physics
Email: mkrendale@gmail.com
Índia, Hubballi, Karnataka
N. Choudhari
Department of Physics
Email: mkrendale@gmail.com
Índia, Manipal, Karnataka
B. Grampurohit
Department of PG Studies in Physics
Email: mkrendale@gmail.com
Índia, Hubballi, Karnataka
M. Rendale
Department of Physics
Autor responsável pela correspondência
Email: mkrendale@gmail.com
Índia, Belagavi, Karnataka
S. Mathad
Department of Physics
Email: mkrendale@gmail.com
Índia, Hubballi, Karnataka
C. Hiremath
Department of PG Studies in Physics
Email: mkrendale@gmail.com
Índia, Hubballi, Karnataka
R. Pujar
Department of PG Studies in Physics
Email: mkrendale@gmail.com
Índia, Hubballi, Karnataka
Arquivos suplementares