Structural and Dielectric Properties of Lead-Free Zr-Doped Barium Titanates


如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅存取

详细

Lead-free BaZrxTi1–xO3 ferroelectrics (x = 0.2, 0.4, 0.6, 0.8) were synthesized by conventional double-sintering technique. The structural, morphological, and dielectric properties of BaZrxTi1–xO3 were investigated as a function of zirconium content x. A single-phase perovskite structure of tetragonal ceramics was identified by XRD. The SEM images of the ferroelectrics exhibit fine grains of varied porosity. All synthesized samples exhibited dielectric dispersion at low frequencies.

作者简介

S. Vasawade

Department of PG Studies in Physics

Email: mkrendale@gmail.com
印度, Hubballi, Karnataka

S. Paramaje

Department of PG Studies in Physics

Email: mkrendale@gmail.com
印度, Hubballi, Karnataka

N. Choudhari

Department of Physics

Email: mkrendale@gmail.com
印度, Manipal, Karnataka

B. Grampurohit

Department of PG Studies in Physics

Email: mkrendale@gmail.com
印度, Hubballi, Karnataka

M. Rendale

Department of Physics

编辑信件的主要联系方式.
Email: mkrendale@gmail.com
印度, Belagavi, Karnataka

S. Mathad

Department of Physics

Email: mkrendale@gmail.com
印度, Hubballi, Karnataka

C. Hiremath

Department of PG Studies in Physics

Email: mkrendale@gmail.com
印度, Hubballi, Karnataka

R. Pujar

Department of PG Studies in Physics

Email: mkrendale@gmail.com
印度, Hubballi, Karnataka

补充文件

附件文件
动作
1. JATS XML

版权所有 © Allerton Press, Inc., 2018