The effect of thermal aging on the strength and the thermoelectric power of the Ti-6Al-4V alloy

Resumo

When the Ti-6Al-4V alloy is overaged at 500-600°C, nanometer-sized α₂ (Ti₃Al) particles can be homogeneously precipitated inside a phases, thereby leading to strength improvement. Widmanstätten and equiaxed microstructures containing fine α₂ (Ti₃Al) particles were obtained by overaging the Ti-6Al-4V alloy. Precipitation of α₂ (Ti₃Al) particles was monitored using thermoelectric power measurements for different aging conditions in the Ti-6Al-4V alloy. Overaging heat treatments were conducted at 515, 545 and 575°C for different aging times. In addition, overaging samples were examined by optical microscopy, scanning electron microscopy and hardness measurements. It was found that the thermoelectric power is very sensitive to the aging process in the two studied Ti-6Al-4V structures.