Impregnation of Graphite with Aluminum under High Pressure
- Authors: Antanovich A.A.1
-
Affiliations:
- Vereshchagin Institute of High-Pressure Physics, RAS
- Issue: No 5 (2024)
- Pages: 97-100
- Section: Articles
- URL: https://journals.rcsi.science/1028-0960/article/view/264389
- DOI: https://doi.org/10.31857/S1028096024050147
- EDN: https://elibrary.ru/FSYKDV
- ID: 264389
Cite item
Abstract
To impregnate graphite of the GMZ brand with liquid aluminum alloy D16, a high-pressure method and apparatus previously used for impregnating carbon frames with liquid coal pitch in the isostatic technology for the production of carbon-carbon composite materials were used. The graphite blank and the amount of aluminum alloy calculated from the initial porosity of graphite were placed in a thin-walled container, degassed in a vacuum furnace, after which the container with the contents was sealed. Thermobaric treatment was carried out at a temperature of 750°C and pressure of 100 and 200 MPa. After finishing the treatment, the density and porosity of the obtained metallographic composites, as well as their compressive strength, were determined. As a result of these thermobaric treatments, the density and compressive strength of the obtained composites increased significantly, and the porosity decreased markedly.
About the authors
A. A. Antanovich
Vereshchagin Institute of High-Pressure Physics, RAS
Author for correspondence.
Email: antanov@hppi.troitsk.ru
Russian Federation, Troitsk
References
- Воронков Б.Д. Подшипники сухого трения. Ленинград: Машиностроение, 1979. 224 с.
- Gulevsky V., Markina N., Zatyamin D., Yudin A., Novoseltsev A., Erizhipov A. // Nor. J. Development. Int. Sci. 2019. V. 36. P. 39.
- Патент SU 1759932 A1. Способ изготовления композиционных материалов. / Волгоградский политехнический институт. Бусалаев И.Д., Соловьев И.А., Рубенчик Ю.И., Гулевский В.А. // БИ 1992. № 33.
- Патент US 3949804. Method of manufacturing a metal-impregnated body. / Toyota Motor Corp. Kaneko Y., Komiyama Y., Kondo K., Noda F., Murakami H., Uchida K. // 1976.
- Wang T.-Ch., Fan T.-X., Zhang D., Zhang G.-D. // Carbon. 2006. V. 44. Iss. 5. P. 900. https://www.doi.org/10.1016/j.carbon.2005.10.022
- Колесников С.А., Антанович А.А., Максимова Д.С., Чеблакова Е.Г. Изостатические технологии в изготовлении углерод-углеродных композиционных материалов. // Научно-исследовательскому институту конструкционных материалов на основе графита – 60 лет. М.: Научные технологии, 2020. С. 19.