New carbon structures in annealed carbon–cadmium film coatings
- 作者: Volodin V.N.1, Tuleushev Y.Z.1, Shabanova T.A.2, Sukurov B.M.3, Zhakanbaev E.A.1
-
隶属关系:
- Institute of Nuclear Physics
- Institute of Geological Sciences
- Center of Earth, Metallurgy and Enrichment Sciences
- 期: 卷 10, 编号 6 (2016)
- 页面: 1187-1191
- 栏目: Article
- URL: https://journals.rcsi.science/1027-4510/article/view/190354
- DOI: https://doi.org/10.1134/S1027451016050621
- ID: 190354
如何引用文章
详细
Carbon–cadmium alloy film coating solid solutions coexisting with amorphous carbon are for the first time obtained via ion-plasma sputtering and the codeposition of ultrafine particles of the above elements onto moving substrates. The concentration boundary of the existence of carbon solid solutions in cadmium is found to be a total carbon content in the coating of 63.5 at % (15.66 wt %). Upon the vacuum heat treatment of carbon–cadmium films with a carbon concentration of more than 57.5 at %, almost total evaporation of cadmium occurs with the formation of an amorphous carbon coating. During annealing at 1100°C, the amorphous carbon is found to crystallize into a new phase with a hexagonal primitive lattice and the parameters а = 0.6405 and с = 0.7828 nm. The face-centered cubic (fcc) phase of carbon with the lattice parameter а = 0.4265 nm is recorded in the nanocrystalline formations. The behavior of the initial film coating components during heating in vacuum is assumed, as well.
作者简介
V. Volodin
Institute of Nuclear Physics
Email: yuriy.tuleushev@mail.ru
哈萨克斯坦, Almaty, 050032
Yu. Tuleushev
Institute of Nuclear Physics
编辑信件的主要联系方式.
Email: yuriy.tuleushev@mail.ru
哈萨克斯坦, Almaty, 050032
T. Shabanova
Institute of Geological Sciences
Email: yuriy.tuleushev@mail.ru
哈萨克斯坦, Almaty, 050010
B. Sukurov
Center of Earth, Metallurgy and Enrichment Sciences
Email: yuriy.tuleushev@mail.ru
哈萨克斯坦, Almaty, 050010
E. Zhakanbaev
Institute of Nuclear Physics
Email: yuriy.tuleushev@mail.ru
哈萨克斯坦, Almaty, 050032
补充文件