Synthesis and Ionic Conductivity of NaZr2(AsO4)x(PO4)3 –x

详细

Arsenate phosphates NaZr₂(AsO₄)_x(PO₄)_{3 –x} are synthesized by the sol–gel method with subsequent annealing at 1123 K. Thus obtained specimens are investigated using X-ray diffraction analysis, IR and impedance spectroscopy. In the NaZr₂(AsO₄)_x(PO₄)_{3 –x} system, continuous solid solution (0 ≤ x ≤ 3) with NaZr₂(PO₄)₃ (NASICON) structure forms. According to the impedance spectroscopy data, an increase of the content of arsenic in the NaZr₂(AsO₄)_x(PO₄)_{3 –x} system leads to an increase of the sodium-ionic conductivity; for NaZr₂(AsO₄)₃, it reaches 8 × 10^–5 S/cm at 773 K. At the same time, the activation energy of conductivity of this material (50 ± 1 kJ/mol) appears to be twice lower than the activation energy of conductivity of NaZr₂(PO₄)₃ (100 ± 1 kJ/mol).