- Авторы: Pet’kov V.1, Shipilov A.1, Borovikova E.2, Stenina I.3, Yaroslavtsev A.2,3
-
Учреждения:
- Lobachevsky State University
- Moscow State University
- Kurnakov Institute of General and Inorganic Chemistry, Russian Academy of Sciences
- Выпуск: Том 55, № 10 (2019)
- Страницы: 1034-1038
- Раздел: Short Communications
- URL: https://journals.rcsi.science/1023-1935/article/view/191128
- DOI: https://doi.org/10.1134/S1023193519100070
- ID: 191128
Цитировать
Аннотация
Arsenate phosphates NaZr2(AsO4)x(PO4)3 –x are synthesized by the sol–gel method with subsequent annealing at 1123 K. Thus obtained specimens are investigated using X-ray diffraction analysis, IR and impedance spectroscopy. In the NaZr2(AsO4)x(PO4)3 –x system, continuous solid solution (0 ≤ x ≤ 3) with NaZr2(PO4)3 (NASICON) structure forms. According to the impedance spectroscopy data, an increase of the content of arsenic in the NaZr2(AsO4)x(PO4)3 –x system leads to an increase of the sodium-ionic conductivity; for NaZr2(AsO4)3, it reaches 8 × 10–5 S/cm at 773 K. At the same time, the activation energy of conductivity of this material (50 ± 1 kJ/mol) appears to be twice lower than the activation energy of conductivity of NaZr2(PO4)3 (100 ± 1 kJ/mol).
Об авторах
V. Pet’kov
Lobachevsky State University
Автор, ответственный за переписку.
Email: petkov@inbox.ru
Россия, Nizhny Novgorod, 603950
A. Shipilov
Lobachevsky State University
Автор, ответственный за переписку.
Email: as-shipilov@yandex.ru
Россия, Nizhny Novgorod, 603950
E. Borovikova
Moscow State University
Email: as-shipilov@yandex.ru
Россия, Moscow
I. Stenina
Kurnakov Institute of General and Inorganic Chemistry, Russian Academy of Sciences
Email: as-shipilov@yandex.ru
Россия, Moscow, 119071
A. Yaroslavtsev
Moscow State University; Kurnakov Institute of General and Inorganic Chemistry, Russian Academy of Sciences
Email: as-shipilov@yandex.ru
Россия, Moscow; Moscow, 119071